The results show that electrode degradation mechanism was basically caused by wear due to fracture of local welding between the electrode tip surface and zinc coated sheet steel happen at electrode surface and alloying between electrode and zinc on zinc coated steel during resistance spot welding zinc coated steel.

结果表明：点焊镀锌钢板时电极的失效机制主要是电极和镀锌板之间局部焊接的断裂发生在电极表面而导致的电极磨损以及电极和镀锌板表面的锌之间的合金化。

Actual thermal cycling curve of welded seam of laser welding is obtained to zinc coated high strength steel.

对激光焊接高强度镀锌钢板时接头上热循环作了试验测定，测出了焊缝热影响区的实际热循环曲线。

The galvanic corrosion of aluminum alloy coupled with different materials, including Q_235 steel, zinc-coated iron plate, copper plate, was studied by free running test in 3.5% NaCl solution.

采用自由测试法测定了铝合金分别与Q235钢、镀锌铁片和铜片三种不同材料组成的电偶在3.5%NaCl水溶液中的电偶电流、腐蚀电位和腐蚀速度。

The cubicle is made of folded high quality aluminum zinc coated steel plate linking with screws.

柜体采用敷铝锌板经过多重折弯而成.

Study on laser welding of zinc coated steel and the effects of zinc vaporization

镀锌板激光焊接工艺及锌行为研究

HDPE with zinc coated steel nail.

HDPE及 优质镀锌钢钉.

The effect of TiC coating in electrode tip surface on spheriform electrode degradation during resistance spot welding zinc coated steel was investigated by SEM, EDX and XRD.

利用SEM、EDX和XRD等方法分析了在点焊镀锌钢板时球形电极表面熔敷TiC涂层对电极失效的影响。